低翘曲性, 耐疲劳性能, 抗溶解性, 韧性良好, 良好的强度, 收缩性低, 电气/电子应用领域, 电器用具, 通信应用

Radici Compounds RN66N50L

聚酰胺66

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

RN66N50L is a nylon 6.6 formulation, nucleated to accelerate crystallization and enable very fast cycle times to be realized, especially in multi-cavity tooling; a special lubricant system is also incorporated for ease of mold release. Compared with a general-purpose product such as RN6650L, this nucleated grade exhibits higher strength and rigidity, but lower practical toughness. Mold shrinkage is also lower, and more isotropic, often resulting in reduced tendency for warpage.

 

RN66N50L is Recognized by Underwriters' Laboratories under File No. E 148796; details of Relative Thermal Indices, and electrical PLC values, are available from Michael Day Enterprises, or on line at www.ul.com/plastics.

 

RN66N50L has also been evaluated according to the requirements of U.L. 1446 and IEC Standard 61857 and is Recognized under U.L. File No. E164279 for use as the Ground Insulation in both Class 130 and Class 155 Electrical Insulation Systems. Full details are available from Michael Day Enterprises, or from UL at data.ul.com/systems.

 

Nylon 6.6 offers a unique combination of strength and toughness, excellent static and dynamic fatigue resistance, natural lubricity and resistance to the effects of a broad range of chemicals, oils and solvents, and is therefore used in such markets as electrical, electronics, communications or appliances where this performance combined with Underwriters' Laboratories Recognition is required.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - MDE PA66 (English)

•  Technical Datasheet (English)

UL 黄卡 2 •  E148796-223588

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

添加剂 • 成核剂 • 润滑剂

• 低翘曲性 • 耐疲劳性能 • 脱模性能良好

• 经润滑 • 耐油性能

性能特点 • 抗溶解性 • 韧性良好 • 有核

• 良好的强度 • 生产阶段，快 • 中等硬度

• 耐化学性良好 • 收缩性低

用途 • 电气/电子应用领域 • 电器用具 • 通信应用

UL 档案号 • E148796

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.14g/cm³ ASTM D792

收缩率 - 流动 (3.18 mm) 1.0 到 1.4% ASTM D955

吸水率 (24 hr) 1.2% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 (屈服, 23°C) 96.5MPa ASTM D638

伸长率 (断裂, 23°C) 15 到 25% ASTM D638

弯曲模量 (23°C) 3170MPa ASTM D790

弯曲强度 (23°C) 128MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 43 到 48J/m ASTM D256

拉伸冲击强度 4 (23°C) 315kJ/m² ASTM D1822

硬度 额定值单位制 测试方法

洛氏硬度 (R 计秤) 123 ASTM D785

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 90.0°C ASTM D648

熔融温度 250 到 265°C ASTM D789

可燃性 额定值单位制 测试方法

UL 阻燃等级 (0.750 mm, ALL) V-2 UL 94

 

Radici Compounds RN66N50L

聚酰胺66

Radici Plastics USA, Inc.

注射 额定值单位制

干燥温度 82.2°C

干燥时间 4.0hr

建议的最大水分含量 0.25%

建议注入量 40 到 70%

螺筒后部温度 282°C

螺筒中部温度 279°C

螺筒前部温度 277°C

加工（熔体）温度 271 到 293°C

模具温度 60.0 到 82.2°C

背压 0.345MPa

螺杆转速 40 到 80rpm

垫层 3.18 到 6.35mm

 

 

 

 

聚酰胺66，PA66 Radici Compounds RN66N50L是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123  微信：13549213581   QQ：15397858 

13549213581 肖生